COMPOSITION
High quality compressed non asbestos fibre jointing sheets based
on aramide and special mineral fibers mixed in a NBR rubber matrix.
This material offers high stress relaxation
(Grade Y), high compressibility and low gas permeability, excellent
characteristics for universal services. Material suitable for use
with air, water, oils, hydrocarbons, gases and common uses. Particularly
suitable for use in compressors, pumps, valves and OEM equipment.
| Technical
Data. |
| COLOUR |
Blue |
| Standard sizes (mm) Other upon request |
1500 x 1500 |
| Standard thickness (mm). Other upon
request |
0,5, 0.8, 1, 1,5,
2, 3 |
| Density
(± 10%) |
1,65
g/cm³ |
| Compressibility
ASTM F-36A |
7%-15% |
| Recovery
ASTM F-36A |
>55% |
| Transverse
tensile strength ASTM F-152 |
12
MPa |
| Gas
permeability DIN 3535/6 |
<0,5
cm³/min |
| Hot creep at 200ºC x wsw/200
(%) |
10-12 |
| Cold compressibility x KSW (%) |
11 |
| Cold recovery x KRW (%) |
3,5 |
| Hot recovery at 200ºC x wsR/200
(%) |
1,0 |
| Thickness
increase ASTM F-146 after: |
| Immersion
in ASTM oil Nš1 5h 150ºC |
<3% |
| Immersion
in ASTM oil Nš3 5h 150ºC |
<7% |
| Immersion
in ASTM fuel B 5h 20ºC |
<8% |
| Typical properties for 2 mm thickness |
| |
|
| PRESSURE-TEMPERATURE
DIAGRAM |
P-T OPERATING GUIDELINES
|
 |
1- Usually satisfactory to use
without reference to Montero. Technical examination is normally
unnecessary.
2- Must refer to Montero for advice. A technical
examination is recommended
3- Area not recommended.
The P-T diagram helps the user or designer
who often knows the operating temperature and pressure to
carry out an initial selection of a suitable material . The
P-T diagram cannot guarantee the suitability of a material
for an application
|
|